Generally speaking hot roll steel has a rougher surface wider tolerances and lower cost.
Cold rolled sheet metal vs hot rolled.
Hot rolled steel is rolled or shaped at a high temperature while cold rolled steel is rolled at room temperature.
Cold rolled has a smooth and shiny finish while hot rolled has a grey and scaly finish.
The main advantages of cold working are.
Cold rolled has sharper corners and more precise dimensions than hot rolled.
Each type of steel has its advantages and disadvantages and costs for the two types of steel are also different.
There are some fundamental differences between these two types of metal.
Whereas cold rolled steel is processed in cold reduction mills followed by annealing and tempering.
In this article we will compare hot rolled vs cold rolled steel sheets.
Cold rolled steel is essentially hot rolled steel that has been through further processing.
Cold worked steels are typically harder and stronger than standard hot rolled steels.
Typically mills take hot rolled steel after it s mostly or completely cooled and work it to its final dimension by either rolling it extruding it or drawing the metal over a mandrel.
Cold rolled steel has an oily or greasy finish very smooth surface and very sharp edges.
As an example a hot rolled steel product may have a yield strength of 235 mpa.
Once hot rolled steel has cooled it is then re rolled at room temperature to achieve more exact dimensions and better surface qualities.
Both hot rolled steel and cold rolled steel start out in essentially the same way and both can have the same grades and specifications.
In comparison a cold rolled steel product with the same chemical composition has a yield strength of 365 mpa.
On the other hand cold rolled steel is processed as hot roll but once it has cooled to room temperature it received additional processing for different benefits.
Basic difference between hot rolled and cold rolled steel is the way they are processed.
During the hot rolling process steel is heated to its melting point while being worked changing the composition of the steel to make it more malleable.
Hot rolling and cold rolling are two methods of shaping steel.
Hot rolled steel involves rolling the steel at high temperatures where cold rolled steel is processed further in cold reduction mills where the material is cooled followed by annealing and or tempers rolling.
The differences between hot rolled steel and cold rolled steel relates to the way these metals are processed at the mill and not the product specification or grade.
Hot rolled steel comes with a scaly surface slightly rounded edges and corners and the surface is non oily.
Thus the yield strength of cold rolled steel is higher than that of hot rolled steel.
In short hot rolled steel is processed at the mill at high temperatures and that s it.
During cold rolling the steel is annealed or exposed to heat and allowed to cool which improves ductility.